有害슬러지 固形化에 따른 重金屬 溶出防止剖의 影饗

• 영문명: The Effect of Unleached Agents on the Stabilization/Solidification of Hazardous Sludge Containing Heavy Metals
• 발행기관: 한국환경보건학회
• 저자명: 이성호
• 간행물 정보: 『한국환경보건학회지』제19권 제2호, 46~54쪽, 전체 9쪽
• 주제분류: 공학 > 환경공학
• 파일형태: PDF
• 발행일자: 1993.06.30

영문 초록

This study was carried out on the stabilized/solidified treatment for the reducing leachability of hazardous heavy metals copper, lead, chromium and cadmium in the hazardous sludge which treated to be unleached heavy metals by sodium diethyl dithiocarbamate. Cement matrix was analyzed for the leachability of 24 hrs and dynamic leaching test, structure and the optimum condition for the stabilization and solidification of the hazardous sludge. In 28 days of curing time the unconfined compressive strength was 21.5 kg/cm$^2$ at the ratio of portland cement (0.5)+fly ash (0.25) and 23.5 kg/cmz at the ratio of portland cement (0.5)+fly ash (0.25) + cake (0.25). High concentration of Pb, Cr and Cd in the sea water and Cu in the distilled water were leached at the dynamic leaching test. The concentration of leaching heavy metals for specimens which were tested 24 hrs were found low leachability with decreasing pH of leachant. According to dynamic leaching test, the low level of copper, lead, cadmium and chromium were leached in the cement matrix with sodium diethyl dithiocarbamate. But the effective diffusion coefficient of unleached cement matrix which was treated sodium diethyl dithiocarbamate was decreased above 2 times than that of cement matrix. The relation of leachant renewal period (Y) and cumulative fraction ion leached (X) was the following regression equations. Solidification with unleached agent. Y$_{Cu}$ = 1413752X + 247, Y$_{Pb}$ = 223501IX + 214, Y$_{Cr}$ = 8310601X - 472, Y$_{Cd}$ = 168787X + 1061 The structure of solidified matrix with X-ray diffraction analysis was composed more Ca(OH)$_2$, Si, Mg(OH)$_2$ and Al in the unleached cement matrix than those in cement matrix.