스플릿 레더 코팅을위한 폴리 카프로 락톤 디올 기반 수성 폴리 우레탄의 제조 및 물리적 특성

• 영문명: Preparation and Physical Properties of Polycaprolactone Diol-based Water-based Polyurethanes for Split Leather Coatings
• 발행기관: 한국응용과학기술학회 (구.한국유화학회)
• 저자명: 이주엽(Lee Joo-Youb)
• 간행물 정보: 『한국응용과학기술학회지』한국응용과학기술학회지 제37권 제1호, 49~55쪽, 전체 7쪽
• 주제분류: 공학 > 화학공학
• 파일형태: PDF
• 발행일자: 2020.02.29

영문 초록

In this study, isophorone diisocyanate (IPDI) and dimethylolbutanoic acid (DMBA) were used on the basis of poly caprolactone diol (3M, 3.5M, 4M, 4.5M) for the synthesis of water-based polyurethanes for coating on skin layers of leather. Tensile strength, elongation, and adhesive strength of the prepared samples were measured. As a result of measuring the tensile strength, the tensile strength was found to be 4.09 kgf / mm2 when 3 moles were applied, and 1.071 kgf / mm2 when 4.5 moles were applied. Elongation was 366 % when 3 moles of PCL were applied, and 709 % at 4.5 moles. Adhesive strength was 2.887 kgf / cm when 3 moles of PCL was applied and 0.998 kgf / cm when 4.5 moles were applied.

목차

1. Introduction

2. Experiment

3. Results and Discussion

4. Conclusion

키워드

polyurethane dispersion tesnile strength adhesive strength elongation