클로로포름을 사용한 전기방사법에 의한 고분자량 폴리비닐카바졸 웹의 제조 및 특성(2)

• 영문명: Preparation of High Molecular Weight P이y(N_Vinyl Carbazole) Web by Electrospinning Using Chloroform and Its Characterization
• 발행기관: 한국산업기술융합학회(구. 산업기술교육훈련학회)
• 저자명: 김희삼(Hee Sam Kim) 김채성(Chae Sung Kim)
• 간행물 정보: 『산업기술연구논문지』산업기술교육훈련논문지 제19권 3호, 63~70쪽, 전체 8쪽
• 주제분류: 공학 > 산업공학
• 파일형태: PDF
• 발행일자: 2014.09.30

영문 초록

In this study, adapting high molecular weight PVCz and controlling three major parameters for electrospinning, we successfully prepared novel PVCz fibrous webs. SEM images showed that the structure and morphology of electrospun PVCz webs depended on processing parameters such as solution viscosity(e.g. concentration and polymer molecular weight), AV, TCD, and the type of solvent. Concentration of poly(N-vinyl carbazole) (PVCz) solution was varied from 3 to 18 wt(%). All electrospinning procedures were carried out at 25 °C room temperature. Applied voltage was ranged from 15 to 30 kV. Tip-to-collector distance(TCD) was varied from 10 to 40cm. In the cases of, using chloroform as a solvent, the fiber diameters in the range from 3.8/mi to ll.Qum were obtained by varying the solution concentration. It was found that the morphology of electrospun PVCz web was strongly correlated with viscosity. At lower solution concentration，webs containing beads and beads-ont으fibers were prepared, while, at higher one, fine and uniform fibers in webs could be formed. Average diameters of fibers in webs were decreased with increases in the applied voltage and TCD.

목차

ᅵ. 서 론

II. 실 험

III. 실험결과 및 고찰

IV. 결 론

참고문헌

키워드

Electrospinning(전기방사) PVCz(폴리비닐카바졸) Web(웹) Applied Voltage(인가전압) Molecular Weight(분자량)